Timken公司所生產(chǎn)的AISI/SAE 4130/4130HW無縫鋼管主要應(yīng)用于海工鉆井平臺上裝配的7,500-15,000psi等級的高壓泥漿管線和高壓水泥管線。

?

一、規(guī)范性引用文件Normative?Reference

ASTM A519 Standard Specification for Seamless Carbon and Alloy Steel Mechanical Tubing

ASME B36.10 Welded and Seamless Wrought Steel Pipe

ASTM A370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products

ASTM E8 Standard Test Methods for Tension Testing of Metallic Materials

ASTM E18 Standard Test Methods for Rockwell Hardness of Metallic Materials

ASTM E23 Standard test methods for Notched bar impact testing of metallic materials

ASTM E112 Standard Test Methods for Determining Average Grain Size

ASTM E213 Standard Practice for Ultrasonic Examination of Metal Pipe and Tubing

NACE MR0175 Metals for Sulfide Stress Cracking and Stress Corrosion Cracking Resistance in Sour Oilfield Environments

?

二、鋼管狀態(tài)及符合的標(biāo)準(zhǔn)?Tube Condition and Standard

無縫鋼管的狀態(tài)為：熱軋- 淬火- 回火- 去應(yīng)力- 去氧化皮

鋼管應(yīng)符合美國ASTM ?A519 《機(jī)械用無縫鋼管-合金鋼管的標(biāo)準(zhǔn)規(guī)范》。

?

三、技術(shù)要求?Technical Specification

1. 化學(xué)成分 Chemistry

2. 機(jī)械性能 Mechanical Property

抗拉強(qiáng)度σ_b≥655 Mpa （95ksi），屈服強(qiáng)度σ_s≥585 Mpa （85ksi），延伸率δ₅≥17%，斷面收縮率Red≥35%，拉伸試樣標(biāo)距段長度為50.8 mm，圓形，取樣位置為管壁中間位置。

——抗拉強(qiáng)度 tensile strength：s_b≥ 655 Mpa；

——屈服強(qiáng)度 yield strength：σ_s≥?585 Mpa；

——伸長率（縱向）elongation (longitudinal)：d₅≥ 17%;

——斷面收縮率 reduction of area：Red≥ 35%;

3. 縱向沖擊功 Longitudinal Impact （可選）

平均縱向沖擊功AK_V≥42 J，單個值A(chǔ)K_V≥30 J，夏比試驗(yàn)，試驗(yàn)溫度0攝氏度，取樣位置為管壁中心。

4. 硬度要求 Hardness

鋼管表面洛氏硬度不超過22HRC， 符合NACE MR 01 75。

5. 鋼管晶粒度 Grain Size：≥5級

6. 鋼管的熱處理 Heat treatment

管材需要淬火+回火狀態(tài)交貨。

7. 鋼管的無損檢測Non-destructive Inspection

鋼管需要對內(nèi)、外徑進(jìn)行探傷，以保證無有害的表面及內(nèi)部缺陷。表面探傷使用Eddy（渦流）探傷方式，內(nèi)徑探傷使用超聲波探傷方式。表面缺陷不超過壁厚的5%，內(nèi)壁缺陷不超過壁厚的5%。

?