利用金相組織觀察(OM)、掃描電鏡分析(SEM)、透射電鏡觀察(TEM)以及硬度測試，研究固溶處理對7B04鋁合金顯微組織及硬度的影響。
固溶處理對7B04鋁合金組織及性能的影響Effects of solution treatment on microstructures and properties of 7B04 aluminum alloy利用金相組織觀察(OM)、掃描電鏡分析(SEM)、透射電鏡觀察(TEM)以及硬度測試，研究固溶處理對7B04鋁合金顯微組織及硬度的影響。結(jié)果表明：實(shí)驗(yàn)合金中的η相(MgZn2)為易溶相，S相(Al2CuMg)為難溶相，含F(xiàn)e雜質(zhì)相為不溶相；進(jìn)行單級固溶處理時，隨著固溶溫度的升高，實(shí)驗(yàn)合金的固溶程度、再結(jié)晶程度和再結(jié)晶晶粒尺寸增加，當(dāng)溫度超過480℃時，出現(xiàn)過燒現(xiàn)象，力學(xué)性能惡化，7B04鋁合金淬火敏感性較高；雙級固溶可有效抑制合金再結(jié)晶、降低合金淬火敏感性，實(shí)驗(yàn)條件下較好的雙級固溶工藝為(450℃, 0.5h)+(490℃, 0.5h)，抑制合金再結(jié)晶效果最佳，經(jīng)120℃時效24h后，硬度達(dá)到最大值，為204HV1。
The influence of solution treatments on the microstructure and hardness of 7B04 aluminum alloy were investigated by means of optical microscopy(OM), scanning election microscopy(SEM), transmission election microscopy(TEM) and hardness test. The results show that there are the soluble phaseη(Mg(Zn,Al,Cu)2), the poorly soluble phaseS(Al2CuMg) and the insoluble impurity Fe phase (Al7Cu2Fe). The degree of solid solution and recrystallization increases with the solution temperature increasing gradually. When the temperature exceeds 480℃, overburning on 7B04 alloy occurs and the properties was weakened, 7B04 alloy has high quench sensitivity. However, double-stage solution can inhibit recrystallization of the alloy and decrease the quench sensitivity effectively. The excellent strengthening effect can be expected at (450℃, 0.5h)+(490℃, 0.5h) among the experiments, by which the recrystallization of the alloy can be restrained mostly and the hardness can reach to 204HV1 after aging at 120℃ for 24h.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博，微信，領(lǐng)英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.