電場對2E12鋁合金中S相析出動力學(xué)的影響
發(fā)布人：上海艾荔艾金屬材料有限公司bt990.com.cn
更新時間：2015-12-22
采用示差掃描量熱法(DSC)，研究2E12鋁合金在190 ℃時效過程中施加強(qiáng)電場(±9 kV/cm)對合金析出的動力學(xué)的影響，并探討電場影響合金時效過程的微觀機(jī)理。
電場對2E12鋁合金中S相析出動力學(xué)的影響Effect of electric field on kinetics of formation of S phase in2E12 aluminum alloy采用示差掃描量熱法(DSC)，研究2E12鋁合金在190 ℃時效過程中施加強(qiáng)電場(±9 kV/cm)對合金析出的動力學(xué)的影響，并探討電場影響合金時效過程的微觀機(jī)理。結(jié)果表明：時效時施加強(qiáng)電場促進(jìn)了合金中Ⅰ型S相向Ⅱ型S相的轉(zhuǎn)變，使得析出峰提前；未施加電場的合金樣品具有更高的過飽和度、析出焓、析出相體積分?jǐn)?shù)及析出速率；強(qiáng)電場作用降低合金中空位與溶質(zhì)原子之間的結(jié)合能，進(jìn)而降低S相析出激活能。根據(jù)DSC結(jié)果對S相析出激活能進(jìn)行Kissinger方法和普適積分法計算發(fā)現(xiàn)，時效過程中施加電場與未施加電場相比，S相激活能分別降低7.9~12.7 kJ/mol和6.8~22.6 kJ/mol。
The influence of electric field (±9 kV/cm) on the aging kinetics and mechanism of 2E12 aluminum alloy during aging at 190 ℃ were investigated by differential scanning calorimetry (DSC). The results show that the transformation of S phase from type Ⅰ to type Ⅱ is promoted by applying electric field. The S phase formation peak in DSC curves under electric field shifts to a lower temperature. The supersaturation degree, formation enthalpy, volume fraction of precipitates and precipitation rate of aged alloy without electric field are higher than those with electric field. The bonding energy between the vacancy and solute atom is decreased by introducing electric field, causing lower activation energies of S phase formation. Based on the DSC results, the activation energies of S phases with electric field in aging are 7.9 ?12.7 kJ/mol and 6.8?22.6 kJ/mol lower than those without electric field calculated by the method of Kissinger and general integration measurement, respectively.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.