通過OM、SEM及布氏硬度分析，研究GWN751K鎂合金在不同狀態(tài)下的顯微組織與性能，確定該合金的雙級均勻化工藝參數(shù)。
GWN751K鎂合金均勻化熱處理Homogenization heat treatment of GWN751K magnesium alloy通過OM、SEM及布氏硬度分析，研究GWN751K鎂合金在不同狀態(tài)下的顯微組織與性能，確定該合金的雙級均勻化工藝參數(shù)。結(jié)果表明：合金經(jīng)過440 ℃、6 h初級均勻化后，共晶組織開始發(fā)生分解，晶粒開始長大；經(jīng)過535 ℃、16 h熱處理后，合金晶粒明顯長大，但元素分布 較為均勻，晶界處僅明顯殘留含Y化合物；均勻化處理使合金的力學(xué)性能得到改善，合金斷裂強度為245 MPa，屈服強度為192 MPa，伸長率為12%，較鑄態(tài)合金的力學(xué)性能均有所提高；合金變形抗力較鑄態(tài)合金的有所增加，這種特性在450 ℃仍保留下來，但差別減小。
The microstructures and properties of the as-cast and homogenized GWN751K magnesium alloy were investigated by optical microscopy, scanning electron microscopy and hardness measurement. The two-step homogenization parameters were determined. The results indicate that the eutectic structures in the as-cast alloy begin to decompose, and the grains begin to grow up after the alloy is homogenized at 440 ℃ for 6 h. After heat treatment at?? 535 ℃ for 16 h, the elements distribute uniformly and the grains grow up obviously, only yttrium element of intermetallic compounds leaves around boundary. The mechanical properties are improved after homogenization, with σb=245 MPa, σ0.2=192 MPa and δ=12%, which are better than those of the as-cast alloy. The flow stress of the homogenized alloy is higher than that of the as-cast alloy and this character is still retained until 450 ℃, but the difference decreases.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.