熱等靜壓溫度對FGH95合金組織和持久性能的影響
發(fā)布人：上海艾荔艾金屬材料有限公司bt990.com.cn
更新時間：2015-12-08
通過對FGH95合金進行不同溫度的熱等靜壓處理、組織形貌觀察及持久性能測試，研究熱等靜壓溫度對合金組織結構與持久性能的影響。
熱等靜壓溫度對FGH95合金組織和持久性能的影響Effects of hot isostatic pressing temperature on?microstructure and stress rupture properties of FGH95 superalloy
通過對FGH95合金進行不同溫度的熱等靜壓處理、組織形貌觀察及持久性能測試，研究熱等靜壓溫度對合金組織結構與持久性能的影響。結果表明：在低于γ′ 相溶解溫度進行熱等靜壓時，粗大γ′ 相沿顆粒邊界區(qū)域不連續(xù)分布；隨熱等靜壓溫度的升高，合金中一次粗大γ′ 相的數(shù)量、尺寸逐漸減小，經1 140 ℃固溶處理后，晶粒尺寸無明顯變化；合金經1 180 ℃熱等靜壓及完全熱處理后，粗大γ′ 相完全溶解及γ′ 相貧化區(qū)消失，晶粒尺寸明顯長大，γ′ 相和細小碳化物沿晶界及晶內彌散析出，因而合金具有較好的持久性能；合金在持久性能測試期間的變形機制是位錯在基體中滑移及剪切γ′ 相。
By means of the hot isostatic pressing treatment (HIP) at the different temperatures, microstructure observation and stress rupture properties measurement, the influence of HIP temperatures on the microstructure and enduring properties of FGH95 nickel-base superalloy were investigated. The results show that, when the HIP temperature is lower than γ′ phase dissolving temperature, coarser γ′ phase discontinuously distributes in the particle boundary regions and the quantity and size of coarser γ′ precipitates decrease gradually as the HIP temperature increasing. No feature of the grain growing up is detected after the alloy is solution treated at 1 140 ℃, and the carbide particles distribute along the grain boundary and in the grain. After HIP-treated at 1 180 ℃ and fully heat treated, the coarser γ′ phase in the alloy is dissolved, the depleted zone of the fine γ′ phase disappears, and the grain size in the alloy obviously increases, and the γ′ phase and fine carbide are dispersedly precipitated within the grains and boundaries, which enhances the enduring properties of the alloy. The deformation mechanisms of the alloy during endurance properties testing are that the dislocations slip in the matrix or shear into γ′ phase.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.